| Product | Cure Time | Shore A Hardness | Specific Gravity | Specific Volume | Color | Tensile Strength | Shrinkage | Elongation At Break | Hundred Percent Modulus | Die B Tear Strength | Useful Temperature Min | Mixed Viscocity | Mix Ratio By Volume | Mix Ratio By Weight | Pot Life | Hundred Percent Modulus | Color | Die B Tear Strength | Mixed Viscocity | Useful Temperature Min | Cure Time | Pot Life | Specific Volume | Specific Gravity | Mix Ratio By Weight | Shrinkage | Mix Ratio By Volume | Tensile Strength | Elongation At Break | Shore A Hardness | Dielectric Strength | Dielectric Strength |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ecoflex™ 00 10 | 4 h. | 00-10 | 1.04 g/cc | 26.6 cu. in./lb. | Translucent | 120 psi | <.001 in. / in. | 800 % | 8 psi | 22 pli | -65 °F | 14,000 cps | 1A:1B | 1A:1B | 30 min. | 8 psi | Translucent | 22 pli | 14,000 cps | -65 °F | 4 h. | 30 min. | 26.6 cu. in./lb. | 1.04 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 120 psi | 800 % | 00-10 | - | - |
| Ecoflex™ 00 20 | 4 h. | 00-20 | 1.07 g/cc | 26.0 cu. in./lb. | Translucent | 160 psi | <.001 in. / in. | 845 % | 8 psi | 30 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 30 min. | 8 psi | Translucent | 30 pli | 3,000 cps | -65 °F | 4 h. | 30 min. | 26.0 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 160 psi | 845 % | 00-20 | - | - |
| Ecoflex™ 00 20 FAST | 1 h. | 00-20 | 1.07 g/cc | 26 cu. in./lb. | Translucent | 160 psi | <.001 in. / in. | 845 % | 8 psi | 30 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 20 min. | 8 psi | Translucent | 30 pli | 3,000 cps | -65 °F | 1 h. | 20 min. | 26 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 160 psi | 845 % | 00-20 | 350 volts/mil | 350 volts/mil |
| Ecoflex™ 00 30 | 4 h. | 00-30 | 1.07 g/cc | 26.0 cu. in./lb. | Translucent | 200 psi | <.001 in. / in. | 900 % | 10 psi | 38 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 45 min. | 10 psi | Translucent | 38 pli | 3,000 cps | -65 °F | 4 h. | 45 min. | 26.0 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 200 psi | 900 % | 00-30 | - | - |
| Ecoflex™ 00 50 | 3 h. | 00-50 | 1.07 g/cc | 25.9 cu. in./lb. | Translucent | 315 psi | <.001 in. / in. | 980 % | 12 psi | 50 pli | -65 °F | 8,000 cps | 1A:1B | 1A:1B | 18 min. | 12 psi | Translucent | 50 pli | 8,000 cps | -65 °F | 3 h. | 18 min. | 25.9 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 315 psi | 980 % | 00-50 | - | - |
Seit über dreißig Jahren suchen wir weltweit nach den hochwertigsten Materialien für Modellbau, Formenbau und Guss.
Von Silikonen und Harzen bis zu Jesmonite und Special-Effects-Materialien — ein sorgfältig kuratiertes Sortiment für Profis, Künstler und Macher.
Unser Vertriebsteam ist bekannt für sein Wissen und Engagement und unterstützt Sie bei Formenbau, Guss, Bildhauerei und Prototyping.
Wir versenden aus unseren Lagern in Amsterdam, Barcelona und Madrid an Kunden in ganz Europa, von Griechenland bis Norwegen.
FormX wurde in Amsterdam gegründet und wuchs von einer lokalen Kunstgießerei zu einem bedeutenden europäischen Lieferanten — mit festen Wurzeln in der Stadt.
FormX ist auf die Versorgung und den spezialisierten Handel mit 3D-Modelliermaterialien im weitesten Sinne des Wortes spezialisiert und verfügt über Lager und Showrooms in Amsterdam, Barcelona und Madrid.